- 熔體流動速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.9
- 缺口沖擊強度: 0.21
- 拉伸強度 [MPa]: 35.9
- 彎曲強度 [MPa]: 19.3
- 彎曲模量 [MPa]: 1.39
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D1505 | ||
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 230 °C | 35 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 71 | 71 | ASTM D-2240 | ||
| Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Tensile Strength, Yield | 35.9 MPa | 5210 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | 490 % | 490 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Yield | 21 % | 21 % | 2 in/min (20 mm/min); ASTM D638 | ||
| Flexural Modulus | 1.39 GPa | 202 ksi | Secant @ 1% strain; ASTM D-790 | ||
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 | ||