- 熔體流動(dòng)速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.9
- 缺口沖擊強(qiáng)度: 0.214
- 拉伸強(qiáng)度 [MPa]: 33.1
- 彎曲模量 [MPa]: 1.28
- 硬度: 98.0
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D-1505 | ||
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 98 | 98 | ASTM D-785 | ||
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | ASTM D-638 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D-638 | ||
| Flexural Modulus | 1.28 GPa | 185 ksi | ASTM D-790 | ||
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D-256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D-648 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||