- 熔體流動速率 [g/10min]: 18.0
- 密度 [g/cm3]: 0.9
- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 34.0
- 彎曲模量 [MPa]: 1.300
- 硬度: 89.0
- 熱變形溫度 [℃]: 82.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 89 | 89 | ASTM D785 |
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.300 GPa | 188.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | |