- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.32
- 缺口沖擊強度: 0.641
- 拉伸強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 2.299
- 硬度: 70.0
- 熱變形溫度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.299 GPa | 333.5 ksi | ASTM D638 |
| Flexural Strength | 39.0 MPa | 5660 psi | ASTM D790 |
| Flexural Modulus | 2.299 GPa | 333.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm | V-0 @Thickness 0.0625 in | UL File #E99379(N) |