- 熔體流動速率 [g/10min]: 18.0
- 密度 [g/cm3]: 0.901
- 缺口沖擊強度: 0.24
- 拉伸強度 [MPa]: 35.2
- 彎曲強度 [MPa]: 18.6
- 彎曲模量 [MPa]: 1.45
- 熱變形溫度 [℃]: 99.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.901 g/cc | 0.0326 lb/in3 | ASTM D1505 | ||
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 230 °C | 18 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Tensile Strength, Yield | 35.2 MPa | 5110 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | 20 % | 20 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Yield | 9.0 % | 9.0 % | 2 in/min (20 mm/min); ASTM D638 | ||
| Flexural Modulus | 1.45 GPa | 210 ksi | Secant @ 1% strain; ASTM D-790 | ||
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 | ||
| Descriptive Properties | |||||