- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.905
- 缺口沖擊強度: 1.33
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 1.24
- 熱變形溫度 [℃]: 103.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ASTM D1505 | ||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 | 83 | ASTM D2240 | ||
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 50 mm/min (2 in./min.); ASTM D638 | ||
| Elongation at Break | >= 200 % | >= 200 % | 50 mm/min (2 in./min.); ASTM D638 | ||
| Elongation at Yield | 14 % | 14 % | 50 mm/min (2 in./min.); ASTM D638 | ||
| Flexural Modulus | 1.24 GPa | 180 ksi | Secant @ 1% strain; ASTM D790 | ||
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||