- 熔體流動速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.9
- 缺口沖擊強度: 0.21
- 拉伸強度 [MPa]: 19.3
- 彎曲強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 0.896
- 硬度: 84.0
- 熱變形溫度 [℃]: 76.1
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 1.13 g/cc | 0.0325 - 0.0408 lb/in3 | Average value: 0.921 g/cc Grade Count:36 |
| Moisture Vapor Transmission | 7.10 - 9.40 cc-mm/m2-24hr-atm | 18.0 - 23.9 cc-mil/100 in2-24hr-atm | Average value: 7.87 cc-mm/m2-24hr-atm Grade Count:3 |
| Oxygen Transmission | 95.0 cc-mm/m2-24hr-atm | 241 cc-mil/100 in2-24hr-atm | Average value: 95.0 cc-mm/m2-24hr-atm Grade Count:3 |
| Thickness | 25.4 - 1000 microns | 1.00 - 39.4 mil | Average value: 553 microns Grade Count:9 |
| Melt Flow | 0.450 - 8.00 g/10 min | 0.450 - 8.00 g/10 min | Average value: 2.35 g/10 min Grade Count:34 |
| Surface Tension | 48.0 dynes/cm | 48.0 dynes/cm | Average value: 48.0 dynes/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 84.0 - 110 | 84.0 - 110 | Average value: 95.5 Grade Count:13 |
| Tensile Strength, Ultimate | 30.0 - 35.9 MPa | 4350 - 5210 psi | Average value: 33.9 MPa Grade Count:3 |
| Film Tensile Strength at Yield, MD | 20.0 - 37.0 MPa | 2900 - 5370 psi | Average value: 28.0 MPa Grade Count:10 |
| Film Tensile Strength at Yield, TD | 16.0 - 36.0 MPa | 2320 - 5220 psi | Average value: 25.3 MPa Grade Count:10 |
| Tensile Strength, Yield | 19.3 - 45.0 MPa | 2800 - 6530 psi | Average value: 34.5 MPa Grade Count:31 |
| Film Elongation at Break, MD | 50.0 - 700 % | 50.0 - 700 % | Average value: 453 % Grade Count:9 |
| Film Elongation at Break, TD | 6.00 - 850 % | 6.00 - 850 % | Average value: 319 % Grade Count:9 |
| Film Elongation at Yield, MD | 14.0 - 24.0 % | 14.0 - 24.0 % | Average value: 18.9 % Grade Count:9 |
| Film Elongation at Yield, TD | 9.00 - 23.0 % | 9.00 - 23.0 % | Average value: 15.4 % Grade Count:9 |
| Elongation at Break | 9.00 - 11.0 % | 9.00 - 11.0 % | Average value: 10.0 % Grade Count:4 |
| Elongation at Yield | 4.00 - 65.0 % | 4.00 - 65.0 % | Average value: 11.8 % Grade Count:26 |
| Modulus of Elasticity | 0.280 - 2.05 GPa | 40.6 - 297 ksi | Average value: 0.710 GPa Grade Count:12 |
| Flexural Modulus | 0.896 - 2.30 GPa | 130 - 334 ksi | Average value: 1.52 GPa Grade Count:35 |
| Izod Impact, Notched | 0.210 - 100 J/cm | 0.393 - 187 ft-lb/in | Average value: 1.75 J/cm Grade Count:35 |
| 0.214 - 2.98984 J/cm @Temperature -20.0 - 4.00 °C | 0.401 - 5.60120 ft-lb/in @Temperature -4.00 - 39.2 °F | Average value: 1.18 J/cm Grade Count:6 | |
| 0.500 - 3.00 J/cm @Temperature -20.0 - 0.000 °C | 0.937 - 5.62 ft-lb/in @Temperature -4.00 - 32.0 °F | Average value: 1.18 J/cm Grade Count:4 | |
| 0.500 - 3.00 J/cm @Thickness 3.20 - 3.20 mm | 0.937 - 5.62 ft-lb/in @Thickness 0.126 - 0.126 in | Average value: 1.18 J/cm Grade Count:4 | |
| Dart Drop, Total Energy | 5.50 - 21.0 J | 4.06 - 15.5 ft-lb | Average value: 9.50 J Grade Count:4 |
| 2.00 - 30.7 J @Temperature -20.0 - 0.000 °C | 1.48 - 22.6 ft-lb @Temperature -4.00 - 32.0 °F | Average value: 12.7 J Grade Count:2 | |
| Tear Strength | 130 - 230 kN/m | 742 - 1310 pli | Average value: 180 kN/m Grade Count:4 |
| Dart drop Total Energy | 55.0 - 60.0 J/cm | 0.103 - 0.112 ft-lb/mil | Average value: 56.7 J/cm Grade Count:3 |
| 20.0 - 55.0 J/cm @Temperature -20.0 - 0.000 °C | 0.0375 - 0.103 ft-lb/mil @Temperature -4.00 - 32.0 °F | Average value: 37.5 J/cm Grade Count:1 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 147 - 165 °C | 297 - 329 °F | Average value: 160 °C Grade Count:11 |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.1 - 130 °C | 169 - 266 °F | Average value: 106 °C Grade Count:32 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 - 60.0 °C | 126 - 140 °F | Average value: 56.8 °C Grade Count:3 |
| Vicat Softening Point | 78.0 - 159 °C | 172 - 318 °F | Average value: 141 °C Grade Count:17 |
| Heat Distortion Temperature | 79.0 - 110 °C | 174 - 230 °F | Average value: 88.1 °C Grade Count:8 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.60 - 46.0 % | 2.60 - 46.0 % | Average value: 19.3 % Grade Count:13 |
| Gloss | 80.0 - 110 % | 80.0 - 110 % | Average value: 93.7 % Grade Count:3 |
| Transmission, Visible | 90.0 - 99.5 % | 90.0 - 99.5 % | Average value: 93.5 % Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 260 °C | 390 - 500 °F | Average value: 235 °C Grade Count:4 |