- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.88
- 缺口沖擊強度: 0.09
- 拉伸強度 [MPa]: 2.07
- 斷裂伸長率 [%]: 20.0
- 彎曲強度 [MPa]: 9.0
- 彎曲模量 [MPa]: 0.0260
- 硬度: 20.0
- 熱變形溫度 [℃]: 55.0
- 脆化溫度 [℃]: -20.0
- 透光率 [%]: 84.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.880 - 2.40 g/cc | 0.0318 - 0.0867 lb/in3 | Average value: 0.934 g/cc Grade Count:742 |
| Water Absorption | 0.000 - 1.00 % | 0.000 - 1.00 % | Average value: 0.0714 % Grade Count:121 |
| Moisture Absorption at Equilibrium | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:58 |
| Water Absorption at Saturation | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:5 |
| Particle Size | 300 - 2500 μm | 300 - 2500 μm | Average value: 900 μm Grade Count:9 |
| Viscosity Measurement | 80.0 - 500000 @Temperature 180 - 180 °C | 80.0 - 500000 @Temperature 356 - 356 °F | Average value: 171000 Grade Count:3 |
| Thickness | 25.4 - 102 microns | 1.00 - 4.00 mil | Average value: 88.9 microns Grade Count:6 |
| Linear Mold Shrinkage | 0.000500 - 0.0250 cm/cm | 0.000500 - 0.0250 in/in | Average value: 0.0132 cm/cm Grade Count:196 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0250 cm/cm | 0.0250 in/in | Average value: 0.0250 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0155 cm/cm | 0.0100 - 0.0155 in/in | Average value: 0.0134 cm/cm Grade Count:5 |
| Melt Flow | 0.200 - 1200 g/10 min | 0.200 - 1200 g/10 min | Average value: 23.2 g/10 min Grade Count:833 |
| Base Resin Melt Index | 0.500 - 50.0 g/10 min @Temperature 230 - 230 °C | 0.500 - 50.0 g/10 min @Temperature 446 - 446 °F | Average value: 15.1 g/10 min Grade Count:17 |
| Ash | 0.00800 - 26.0 % | 0.00800 - 26.0 % | Average value: 1.38 % Grade Count:20 |
| Collected Volatile Condensable Material | 0.0500 - 3.00 % | 0.0500 - 3.00 % | Average value: 0.446 % Grade Count:25 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 20.0 - 118 | 20.0 - 118 | Average value: 96.0 Grade Count:394 |
| Hardness, Shore D | 40.0 - 83.0 | 40.0 - 83.0 | Average value: 69.8 Grade Count:88 |
| Ball Indentation Hardness | 62.0 - 106 MPa | 8990 - 15400 psi | Average value: 85.5 MPa Grade Count:15 |
| Tensile Strength, Ultimate | 9.00 - 80.0 MPa | 1310 - 11600 psi | Average value: 30.3 MPa Grade Count:175 |
| 10.0 - 23.0 MPa @Temperature 60.0 - 120 °C | 1450 - 3340 psi @Temperature 140 - 248 °F | Average value: 16.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 2.07 - 369 MPa | 300 - 53500 psi | Average value: 32.1 MPa Grade Count:766 |
| Film Elongation at Break, MD | 93.0 - 530 % | 93.0 - 530 % | Average value: 258 % Grade Count:3 |
| Elongation at Break | 3.00 - 900 % | 3.00 - 900 % | Average value: 160 % Grade Count:281 |
| Elongation at Yield | 3.50 - 100 % | 3.50 - 100 % | Average value: 11.0 % Grade Count:562 |
| Modulus of Elasticity | 0.00800 - 8.25 GPa | 1.16 - 1200 ksi | Average value: 1.75 GPa Grade Count:223 |
| Tenacity | 0.203 - 0.441 N/tex | 2.30 - 5.00 g/denier | Average value: 0.308 N/tex Grade Count:8 |
| Flexural Yield Strength | 20.0 - 180 MPa | 2900 - 26100 psi | Average value: 44.6 MPa Grade Count:57 |
| Flexural Modulus | 0.0260 - 12.4 GPa | 3.77 - 1800 ksi | Average value: 1.44 GPa Grade Count:715 |
| 0.350 - 0.680 GPa @Temperature 60.0 - 120 °C | 50.8 - 98.6 ksi @Temperature 140 - 248 °F | Average value: 0.472 GPa Grade Count:2 | |
| Compressive Yield Strength | 34.5 - 55.2 MPa | 5000 - 8000 psi | Average value: 39.0 MPa Grade Count:8 |
| Compressive Modulus | 1.38 GPa | 200 ksi | Average value: 1.38 GPa Grade Count:6 |
| Shear Modulus | 0.680 - 0.920 GPa | 98.6 - 133 ksi | Average value: 0.757 GPa Grade Count:10 |
| Secant Modulus | 0.0000689 - 2.20 GPa | 0.0100 - 319 ksi | Average value: 1.23 GPa Grade Count:3 |
| 0.0000344738 - 0.0000344738 GPa @Temperature -20.0 - -20.0 °C | 0.00500008 - 0.00500008 ksi @Temperature -4.00 - -4.00 °F | Average value: 0.0000345 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.0900 J/cm - NB | 0.169 ft-lb/in - NB | Average value: 0.764 J/cm Grade Count:629 |
| 0.0400 - 1.17458 J/cm @Temperature -40.0 - 0.000 °C | 0.0749 - 2.20047 ft-lb/in @Temperature -40.0 - 32.0 °F | Average value: 0.476 J/cm Grade Count:62 | |
| 1.00 - 1.35 J/cm @Temperature -20.0 - -20.0 °C | 1.87 - 2.53 ft-lb/in @Temperature -4.00 - -4.00 °F | Average value: 0.476 J/cm Grade Count:2 | |
| 1.00 - 1.35 J/cm @Diameter 3.17 - 3.17 mm | 1.87 - 2.53 ft-lb/in @Diameter 0.125 - 0.125 in | Average value: 0.476 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 0.196 J/cm - NB | 0.367 ft-lb/in - NB | Average value: 8.39 J/cm Grade Count:57 |
| 2.1356 - 2.1356 J/cm @Temperature -18.0 - -18.0 °C | 4.0009 - 4.0009 ft-lb/in @Temperature -0.400 - -0.400 °F | Average value: 2.14 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 2.00 - 56.0 kJ/m2 | 0.952 - 26.6 ft-lb/in2 | Average value: 7.89 kJ/m2 Grade Count:74 |
| 1.10 - 8.00 kJ/m2 @Temperature -40.0 - 2.00 °C | 0.523 - 3.81 ft-lb/in2 @Temperature -40.0 - 35.6 °F | Average value: 4.02 kJ/m2 Grade Count:26 | |
| Izod Impact, Unnotched (ISO) | NB | NB | Grade Count:6 |
| Charpy Impact Unnotched | 0.300 J/cm2 - NB | 1.43 ft-lb/in2 - NB | Average value: 7.62 J/cm2 Grade Count:116 |
| 0.700 J/cm2 - NB @Temperature -50.0 - -20.0 °C | 3.33 ft-lb/in2 - NB @Temperature -58.0 - -4.00 °F | Average value: 4.06 J/cm2 Grade Count:94 | |
| Charpy Impact, Notched | 0.200 - 9.50 J/cm2 | 0.952 - 45.2 ft-lb/in2 | Average value: 1.11 J/cm2 Grade Count:121 |
| 0.130 - 1.70 J/cm2 @Temperature -30.0 - 10.0 °C | 0.619 - 8.09 ft-lb/in2 @Temperature -22.0 - 50.0 °F | Average value: 0.367 J/cm2 Grade Count:85 | |
| Gardner Impact | 0.904 - 40.7 J | 0.667 - 30.0 ft-lb | Average value: 11.5 J Grade Count:48 |
| 1.99983 - 30.393 J @Temperature -30.0 - -18.0 °C | 1.47500 - 22.417 ft-lb @Temperature -22.0 - -0.400 °F | Average value: 19.9 J Grade Count:24 | |
| 15.0225 - 23.9528 J @Temperature -30.0 - -30.0 °C | 11.0800 - 17.6667 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 19.9 J Grade Count:8 | |
| 15.0225 - 23.9528 J @Thickness 3.17 - 3.20 mm | 11.0800 - 17.6667 ft-lb @Thickness 0.125 - 0.126 in | Average value: 19.9 J Grade Count:8 | |
| Falling Dart Impact | 4.98 - 28.0 J | 3.67 - 20.7 ft-lb | Average value: 10.8 J Grade Count:5 |
| Coefficient of Friction | 0.250 | 0.250 | Average value: 0.250 Grade Count:6 |
| Tensile Creep Modulus, 1 hour | 550 - 700 MPa | 79800 - 102000 psi | Average value: 657 MPa Grade Count:7 |
| Tensile Creep Modulus, 1000 hours | 220 - 440 MPa | 31900 - 63800 psi | Average value: 349 MPa Grade Count:7 |
| Tear Strength | 20.2 - 226 kN/m | 115 - 1290 pli | Average value: 102 kN/m Grade Count:7 |
| Compression Set | 16.0 - 65.0 % | 16.0 - 65.0 % | Average value: 33.2 % Grade Count:4 |
| Film Tensile Strength at Break, MD | 3.10 - 152 MPa | 450 - 22000 psi | Average value: 70.1 MPa Grade Count:3 |
| Tangent Modulus | 1290 - 3260 MPa | 187000 - 472000 psi | Average value: 1920 MPa Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+18 ohm-cm | 1000 - 1.00e+18 ohm-cm | Average value: 1.23e+17 ohm-cm Grade Count:104 |
| Surface Resistance | 100 - 1.00e+15 ohm | 100 - 1.00e+15 ohm | Average value: 1.23e+14 ohm Grade Count:95 |
| Static Decay | 0.0100 - 20.0 sec | 0.0100 - 20.0 sec | Average value: 2.02 sec Grade Count:11 |
| Dielectric Constant | 2.20 - 2.38 | 2.20 - 2.38 | Average value: 2.30 Grade Count:63 |
| Dielectric Strength | 19.7 - 140 kV/mm | 500 - 3560 kV/in | Average value: 128 kV/mm Grade Count:65 |
| Dissipation Factor | 0.0000700 - 0.00300 | 0.0000700 - 0.00300 | Average value: 0.000410 Grade Count:61 |
| Arc Resistance | 88.0 - 136 sec | 88.0 - 136 sec | Average value: 104 sec Grade Count:3 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:76 |
| Tribocharge | 10.0 V | 10.0 V | Average value: 10.0 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 185 μm/m-°C | 10.0 - 103 μin/in-°F | Average value: 114 μm/m-°C Grade Count:106 |
| Melting Point | 61.0 - 180 °C | 142 - 356 °F | Average value: 160 °C Grade Count:199 |
| Crystallization Temperature | 110 - 115 °C | 230 - 239 °F | Average value: 111 °C Grade Count:5 |
| Maximum Service Temperature, Air | 65.0 - 125 °C | 149 - 257 °F | Average value: 78.3 °C Grade Count:26 |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 - 266 °C | 131 - 511 °F | Average value: 102 °C Grade Count:634 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.0 - 172 °C | 98.6 - 341 °F | Average value: 64.1 °C Grade Count:250 |
| Vicat Softening Point | 35.0 - 158 °C | 95.0 - 316 °F | Average value: 120 °C Grade Count:282 |
| Heat Distortion Temperature | 85.0 - 115 °C | 185 - 239 °F | Average value: 97.5 °C Grade Count:8 |
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | Average value: -30.0 °C Grade Count:5 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | Average value: -20.0 °C Grade Count:16 |
| UL RTI, Electrical | 65.0 - 221 °C | 149 - 430 °F | Average value: 147 °C Grade Count:5 |
| UL RTI, Mechanical with Impact | 65.0 - 221 °C | 149 - 430 °F | Average value: 147 °C Grade Count:5 |
| UL RTI, Mechanical without Impact | 65.0 - 221 °C | 149 - 430 °F | Average value: 147 °C Grade Count:5 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:81 |
| Oxygen Index | 24.0 - 30.0 % | 24.0 - 30.0 % | Average value: 26.3 % Grade Count:6 |
| Shrinkage | 1.05 - 2.00 % | 1.05 - 2.00 % | Average value: 1.36 % Grade Count:23 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.200 - 91.0 % | 0.200 - 91.0 % | Average value: 34.4 % Grade Count:55 |
| Gloss | 30.0 - 160 % | 30.0 - 160 % | Average value: 65.3 % Grade Count:20 |
| Yellow Index | 0.000300 - 2.44 % | 0.000300 - 2.44 % | Average value: 0.669 % Grade Count:6 |
| Transmission, Visible | 84.0 - 90.0 % | 84.0 - 90.0 % | Average value: 89.6 % Grade Count:25 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 87.8 - 274 °C | 190 - 525 °F | Average value: 208 °C Grade Count:41 |
| Nozzle Temperature | 204 - 235 °C | 400 - 455 °F | Average value: 212 °C Grade Count:10 |
| Melt Temperature | 145 - 320 °C | 293 - 608 °F | Average value: 209 °C Grade Count:87 |
| Mold Temperature | 4.00 - 91.0 °C | 39.2 - 196 °F | Average value: 41.0 °C Grade Count:81 |
| Roll Temperature | 40.0 - 50.0 °C | 104 - 122 °F | Average value: 43.3 °C Grade Count:5 |
| Drying Temperature | 60.0 - 100 °C | 140 - 212 °F | Average value: 77.2 °C Grade Count:23 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.53 hour Grade Count:29 |
| Moisture Content | 0.0500 - 1.00 % | 0.0500 - 1.00 % | Average value: 0.620 % Grade Count:15 |
| Injection Pressure | 2.76 - 103 MPa | 400 - 15000 psi | Average value: 58.9 MPa Grade Count:32 |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | Average value: 5.17 MPa Grade Count:6 |
| Back Pressure | 0.172 - 1.03 MPa | 24.9 - 150 psi | Average value: 0.603 MPa Grade Count:10 |
| Shelf Life | 12.0 Month | 12.0 Month | Average value: 12.0 Month Grade Count:5 |