- 密度 [g/cm3]: 1.15
- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 16.5
- 斷裂伸長率 [%]: 28.3
- 彎曲強度 [MPa]: 117.0
- 彎曲模量 [MPa]: 2.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.50 g/cc | 0.0415 - 0.0542 lb/in3 | Average value: 1.44 g/cc Grade Count:14 |
| Filler Content | 60.0 % | 60.0 % | Average value: 60.0 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00376 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 117 - 280 MPa | 17000 - 40600 psi | Average value: 157 MPa Grade Count:7 |
| 90.0 - 90.0 MPa @Temperature 80.0 - 80.0 °C | 13100 - 13100 psi @Temperature 176 - 176 °F | Average value: 90.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 16.5 - 150 MPa | 2400 - 21800 psi | Average value: 115 MPa Grade Count:6 |
| Elongation at Break | 1.00 - 2.50 % | 1.00 - 2.50 % | Average value: 1.74 % Grade Count:12 |
| 2.10 - 2.10 % @Temperature 80.0 - 80.0 °C | 2.10 - 2.10 % @Temperature 176 - 176 °F | Average value: 2.10 % Grade Count:1 | |
| Modulus of Elasticity | 6.30 - 25.1 GPa | 914 - 3640 ksi | Average value: 14.0 GPa Grade Count:12 |
| 9.50 - 9.50 GPa @Temperature 80.0 - 80.0 °C | 1380 - 1380 ksi @Temperature 176 - 176 °F | Average value: 9.50 GPa Grade Count:1 | |
| Flexural Yield Strength | 28.3 - 420 MPa | 4100 - 60900 psi | Average value: 215 MPa Grade Count:13 |
| 140 - 140 MPa @Temperature 80.0 - 80.0 °C | 20300 - 20300 psi @Temperature 176 - 176 °F | Average value: 140 MPa Grade Count:1 | |
| Flexural Modulus | 2.41 - 24.1 GPa | 350 - 3500 ksi | Average value: 12.9 GPa Grade Count:13 |
| 9.50 - 9.50 GPa @Temperature 80.0 - 80.0 °C | 1380 - 1380 ksi @Temperature 176 - 176 °F | Average value: 9.50 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.320 - 3.42 J/cm | 0.600 - 6.41 ft-lb/in | Average value: 2.49 J/cm Grade Count:6 |
| Charpy Impact Unnotched | 4.50 - 8.00 J/cm2 | 21.4 - 38.1 ft-lb/in2 | Average value: 6.58 J/cm2 Grade Count:5 |
| 4.50 - 9.00 J/cm2 @Temperature -30.0 - -20.0 °C | 21.4 - 42.8 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 6.46 J/cm2 Grade Count:5 | |
| Charpy Impact, Notched | 1.10 - 3.96 J/cm2 | 5.24 - 18.8 ft-lb/in2 | Average value: 2.68 J/cm2 Grade Count:6 |
| 0.900 - 5.00 J/cm2 @Temperature -30.0 - -20.0 °C | 4.28 - 23.8 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 2.46 J/cm2 Grade Count:5 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 160 - 170 °C | 320 - 338 °F | Average value: 165 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 - 175 °C | 185 - 347 °F | Average value: 153 °C Grade Count:12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 30.0 - 70.0 °C | 86.0 - 158 °F | Average value: 50.0 °C Grade Count:3 |
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Average value: 35.0 °C Grade Count:3 |
| Die Temperature | 240 - 250 °C | 464 - 482 °F | Average value: 245 °C Grade Count:3 |
| Melt Temperature | 199 - 270 °C | 390 - 518 °F | Average value: 236 °C Grade Count:6 |
| Mold Temperature | 37.8 - 90.0 °C | 100 - 194 °F | Average value: 72.2 °C Grade Count:3 |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Average value: 90.0 °C Grade Count:6 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:4 |
| Moisture Content | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.155 % Grade Count:4 |
| Injection Pressure | 60.0 - 140 MPa | 8700 - 20300 psi | Average value: 95.2 MPa Grade Count:5 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | Average value: 60.0 MPa Grade Count:3 |
| Back Pressure | 3.00 MPa | 435 psi | Average value: 3.00 MPa Grade Count:3 |
| Screw Speed | 25.0 - 50.0 rpm | 25.0 - 50.0 rpm | Average value: 36.7 rpm Grade Count:3 |
| Hot-Working Temperature | 230 - 270 °C | 446 - 518 °F | Average value: 250 °C Grade Count:3 |