- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.886
- 缺口沖擊強度: 0.11
- 拉伸強度 [MPa]: 19.0
- 斷裂伸長率 [%]: 28.0
- 彎曲強度 [MPa]: 13.8
- 彎曲模量 [MPa]: 0.620
- 硬度: 57.0
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 1.84 g/cc | 0.0320 - 0.0665 lb/in3 | Average value: 0.917 g/cc Grade Count:170 |
| Filler Content | 12.0 - 25.0 % | 12.0 - 25.0 % | Average value: 19.0 % Grade Count:3 |
| Water Absorption | 0.000 - 0.100 % | 0.000 - 0.100 % | Average value: 0.0183 % Grade Count:12 |
| Moisture Absorption at Equilibrium | 0.000 - 0.0500 % | 0.000 - 0.0500 % | Average value: 0.0200 % Grade Count:3 |
| Water Absorption at Saturation | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0820 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00900 - 0.0250 cm/cm | 0.00900 - 0.0250 in/in | Average value: 0.0153 cm/cm Grade Count:17 |
| Melt Flow | 0.250 - 1480 g/10 min | 0.250 - 1480 g/10 min | Average value: 39.8 g/10 min Grade Count:182 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 57.0 - 120 | 57.0 - 120 | Average value: 93.2 Grade Count:60 |
| Hardness, Shore D | 49.0 - 81.0 | 49.0 - 81.0 | Average value: 71.2 Grade Count:35 |
| Ball Indentation Hardness | 67.0 - 75.0 MPa | 9720 - 10900 psi | Average value: 70.7 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 13.8 - 460 MPa | 2000 - 66700 psi | Average value: 94.0 MPa Grade Count:44 |
| Tensile Strength, Yield | 19.0 - 42.1 MPa | 2760 - 6110 psi | Average value: 32.9 MPa Grade Count:126 |
| Film Elongation at Break, MD | 530 - 700 % | 530 - 700 % | Average value: 590 % Grade Count:3 |
| Elongation at Break | 8.00 - 750 % | 8.00 - 750 % | Average value: 225 % Grade Count:41 |
| Elongation at Yield | 1.60 - 150 % | 1.60 - 150 % | Average value: 15.1 % Grade Count:103 |
| Modulus of Elasticity | 0.680 - 3.60 GPa | 98.6 - 522 ksi | Average value: 1.47 GPa Grade Count:40 |
| Tenacity | 0.185 - 0.512 N/tex | 2.10 - 5.80 g/denier | Average value: 0.403 N/tex Grade Count:12 |
| Flexural Yield Strength | 28.0 - 55.0 MPa | 4060 - 7980 psi | Average value: 36.9 MPa Grade Count:8 |
| Flexural Modulus | 0.620 - 3.20 GPa | 89.9 - 464 ksi | Average value: 1.42 GPa Grade Count:152 |
| Compressive Yield Strength | 4.00 - 14.0 MPa | 580 - 2030 psi | Average value: 10.0 MPa Grade Count:3 |
| Izod Impact, Notched | 0.110 - 5340 J/cm | 0.206 - 10000 ft-lb/in | Average value: 0.748 J/cm Grade Count:105 |
| 0.150 - 0.686465 J/cm @Temperature -30.0 - 0.000 °C | 0.281 - 1.28603 ft-lb/in @Temperature -22.0 - 32.0 °F | Average value: 0.289 J/cm Grade Count:13 | |
| Izod Impact, Unnotched | 0.392 - 15.9 J/cm | 0.735 - 29.8 ft-lb/in | Average value: 9.00 J/cm Grade Count:8 |
| 2.02882 - 2.1356 J/cm @Temperature -18.0 - -18.0 °C | 3.80081 - 4.0009 ft-lb/in @Temperature -0.400 - -0.400 °F | Average value: 2.06 J/cm Grade Count:3 | |
| Izod Impact, Notched (ISO) | 3.00 - 80.0 kJ/m2 | 1.43 - 38.1 ft-lb/in2 | Average value: 15.8 kJ/m2 Grade Count:17 |
| 7.00 - 9.00 kJ/m2 @Temperature -20.0 - -20.0 °C | 3.33 - 4.28 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 8.00 kJ/m2 Grade Count:3 | |
| Charpy Impact Unnotched | 0.800 J/cm2 - NB | 3.81 ft-lb/in2 - NB | Average value: 50.4 J/cm2 Grade Count:12 |
| 1.20 - 9.00 J/cm2 @Temperature -20.0 - 0.000 °C | 5.71 - 42.8 ft-lb/in2 @Temperature -4.00 - 32.0 °F | Average value: 4.47 J/cm2 Grade Count:3 | |
| Charpy Impact, Notched | 0.300 - 55.0 J/cm2 | 1.43 - 262 ft-lb/in2 | Average value: 5.13 J/cm2 Grade Count:30 |
| 0.100 - 26.0 J/cm2 @Temperature -20.0 - 0.000 °C | 0.476 - 124 ft-lb/in2 @Temperature -4.00 - 32.0 °F | Average value: 2.79 J/cm2 Grade Count:17 | |
| Gardner Impact | 1.00 - 36.6 J | 0.738 - 27.0 ft-lb | Average value: 13.4 J Grade Count:11 |
| 1.00 - 1.00 J @Temperature -30.0 - -30.0 °C | 0.738 - 0.738 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.00 J Grade Count:1 | |
| Film Tensile Strength at Break, MD | 20.7 - 55.5 MPa | 3000 - 8050 psi | Average value: 41.4 MPa Grade Count:3 |
| Tangent Modulus | 1240 - 1620 MPa | 180000 - 235000 psi | Average value: 1370 MPa Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+18 ohm-cm | 1000 - 1.00e+18 ohm-cm | Average value: 2.44e+17 ohm-cm Grade Count:14 |
| Surface Resistance | 6.00 - 1.00e+14 ohm | 6.00 - 1.00e+14 ohm | Average value: 3.88e+13 ohm Grade Count:8 |
| Dielectric Constant | 2.20 - 2.30 | 2.20 - 2.30 | Average value: 2.25 Grade Count:8 |
| Dielectric Strength | 19.7 - 100 kV/mm | 500 - 2540 kV/in | Average value: 56.3 kV/mm Grade Count:5 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Oxidation Induction Time | >= 10.0 min @Temperature 200 - 200 °C | >= 10.0 min @Temperature 392 - 392 °F | Average value: 10.0 min Grade Count:1 |
| CTE, linear | 1.50 - 198 μm/m-°C | 0.833 - 110 μin/in-°F | Average value: 106 μm/m-°C Grade Count:14 |
| 100 - 100 μm/m-°C @Temperature 100 - 100 °C | 55.6 - 55.6 μin/in-°F @Temperature 212 - 212 °F | Average value: 100 μm/m-°C Grade Count:1 | |
| Thermal Conductivity | 0.202 - 0.400 W/m-K | 1.40 - 2.78 BTU-in/hr-ft2-°F | Average value: 0.249 W/m-K Grade Count:7 |
| Melting Point | 130 - 174 °C | 266 - 345 °F | Average value: 160 °C Grade Count:44 |
| Maximum Service Temperature, Air | 65.0 - 140 °C | 149 - 284 °F | Average value: 104 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 129 °C | 140 - 264 °F | Average value: 97.2 °C Grade Count:111 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.8 - 110 °C | 118 - 230 °F | Average value: 60.8 °C Grade Count:33 |
| Vicat Softening Point | 60.0 - 156 °C | 140 - 313 °F | Average value: 131 °C Grade Count:56 |
| Heat Distortion Temperature | 80.0 - 119 °C | 176 - 246 °F | Average value: 101 °C Grade Count:11 |
| Minimum Service Temperature, Air | -30.0 - 2.00 °C | -22.0 - 35.6 °F | Average value: -8.00 °C Grade Count:6 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:14 |
| Glow Wire Test | 750 - 960 °C | 1380 - 1760 °F | Average value: 820 °C Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.00 - 46.0 % | 2.00 - 46.0 % | Average value: 18.8 % Grade Count:13 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 120 - 268 °C | 248 - 514 °F | Average value: 217 °C Grade Count:15 |
| Die Temperature | 200 - 310 °C | 392 - 590 °F | Average value: 240 °C Grade Count:10 |
| Melt Temperature | 160 - 330 °C | 320 - 626 °F | Average value: 227 °C Grade Count:32 |
| Head Temperature | 200 - 230 °C | 392 - 446 °F | Average value: 215 °C Grade Count:7 |