- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.14
- 缺口沖擊強度: 1.07
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 2.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 38.6 MPa | 5600 psi | ASTM D-638 |
| Elongation at Break | 40 % | 40 % | ASTM D-638 |
| Modulus of Elasticity | 1.86 GPa | 270 ksi | ASTM D-638 |
| Flexural Strength | 66.2 MPa | 9600 psi | ASTM D-790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm | 2.00 ft-lb/in @Thickness 0.250 in | ASTM D-256 |
| Gardner Impact | 9.04 J @Thickness 3.17 mm | 6.67 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 μm/m-°C | 33.3 μin/in-°F | ASTM D-696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D-648 |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D-1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 3.0 % | <= 3.0 % | ASTM D-1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D-1003 |