- 熔體流動速率 [g/10min]: 4.5
- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 0.481
- 透光率 [%]: 91.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 4.5 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 50.3 MPa | 7300 psi | ASTM D-638 |
| Elongation at Break | 5.3 % | 5.3 % | ASTM D-638 |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | ASTM D-638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D-790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm | 0.900 ft-lb/in @Thickness 0.250 in | ASTM D-256 |
| Gardner Impact | 3.05 J @Thickness 3.17 mm | 2.25 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 μm/m-°C | 38.9 μin/in-°F | ASTM D-696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.9 °C | 174 °F | ASTM D-648 |
| Vicat Softening Point | 112 °C | 233 °F | ASTM D-1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.8 % | <= 1.8 % | ASTM D-1003 |
| Transmission, Visible | 91.3 % | 91.3 % | ASTM D-1003 |