- 密度 [g/cm3]: 1.36
- 彎曲模量 [MPa]: 8.80
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.0090 cm/cm | 0.0090 in/in | Across Flow; ISO 2577 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 @Time 15.0 sec | 80 @Time 0.00417 hour | ASTM D2240 |
| Tensile Strength at Break | <= 160 MPa | <= 23200 psi | ISO/R527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO/R527 |
| Flexural Strength | <= 230 MPa | <= 33400 psi | ISO 178 |
| Flexural Modulus | 8.80 GPa @Temperature 23.0 °C | 1280 ksi @Temperature 73.4 °F | ISO 178 |
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 215 °C @Load 5.001 kg | 419 °F @Load 11.03 lb | 50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Glow Wire Test | 650 °C @Thickness 2.00 mm | 1200 °F @Thickness 0.0787 in | IEC 695-2-1 |