- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 0.587
- 透光率 [%]: 90.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D-792 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 | ||
| Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C | 2.8 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 42.1 MPa | 6100 psi | ASTM D-638 | ||
| Elongation at Break | 37 % | 37 % | ASTM D-638 | ||
| Modulus of Elasticity | 2.03 GPa | 295 ksi | ASTM D-638 | ||
| Flexural Strength | 61.4 MPa | 8900 psi | ASTM D-790 | ||
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm | 1.10 ft-lb/in @Thickness 0.250 in | ASTM D-256 | ||
| Gardner Impact | 6.21 J @Thickness 3.17 mm | 4.58 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 μm/m-°C | 66.7 μin/in-°F | ASTM D-696 | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | UL-746 ABC | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | ASTM D-648 | ||
| Vicat Softening Point | 108 °C | 227 °F | ASTM D-1525 | ||
| Flammability, UL94 | HB | HB | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 1.8 % | <= 1.8 % | ASTM D-1003 | ||
| Transmission, Visible | 90.8 % | 90.8 % | ASTM D-1003 | ||
| Descriptive Properties | |||||
| 3-Year Weathering | Listed | SAE J 576 (AMECA) | |||