- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 1.21
- 缺口沖擊強度: 1.23
- 斷裂伸長率 [%]: 109
- 彎曲模量 [MPa]: 2.83
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Melt Flow | 1.8 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.8 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Flexural Yield Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Thickness 6.35 mm | 2.30 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | 0.25 inch; ASTM D648 |