- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 1.1
- 拉伸強度 [MPa]: 39.0
- 斷裂伸長率 [%]: 57.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 46 | 46 | Method A; ASTM D785 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ASTM D638 |
| Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
| Flexural Yield Strength | 57.0 MPa | 8270 psi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| 0.500 J/cm @Temperature -18.0 °C | 0.937 ft-lb/in @Temperature -0.400 °F | ASTM D256 | |
| Gardner Impact | 5.30 J | 3.91 ft-lb | reported as J/cm; ASTM D3029-GB, unpainted |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 μm/m-°C @Temperature -18.0 - 38.0 °C | 50.0 μin/in-°F @Temperature -0.400 - 100 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | annealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 154 °C | 309 °F | Optimal Thermoforming temperature for sheet 0.25-1.0 cm (0.10-0.39 in) |