- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | Exxon Method |
| Thickness | 76.2 microns | 3.00 mil | |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.90 MPa | 1290 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.20 MPa | 1190 psi | ASTM D882 |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Secant Modulus, MD | 0.152 GPa | 22.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.193 GPa | 28.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 1.30 g/micron | 33.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.64 g/micron | 67.0 g/mil | ASTM D1922 |
| Dart Drop | 3.94 g/micron | 100 g/mil | F50; ASTM D1709 |
| Dart drop Test | 300 g | 0.662 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 107 °C | 225 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 20 % | 20 % | ASTM D1003 |
| Gloss | 40 % | 40 % | 45°, ASTM D-2457 |