| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | |||
| Filler Content | 30 % | 30 % | |||
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | |||
| Elongation at Break | 2.0 % | 2.0 % | |||
| Tensile Modulus | 11.6 GPa | 1680 ksi | |||
| Flexural Yield Strength | 185 MPa | 26800 psi | |||
| Flexural Modulus | 10.9 GPa | 1580 ksi | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | |||
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | |||
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |||
| Dielectric Constant | 3.2 | 3.2 | |||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | ASTM D145 | ||
| Dissipation Factor | 0.0020 | 0.0020 | IEC 60250 | ||
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 | ||
| Hot Wire Ignition, HWI | 30 - 60 sec @Thickness 1.50 mm |
30 - 60 sec @Thickness 0.0591 in |
UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.33 µin/in-°F @Temperature -22.0 - 86.0 °F |
|||
| CTE, linear, Transverse to Flow | 47.0 µm/m-°C | 26.1 µin/in-°F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |||
| UL RTI, Electrical | 125 °C | 257 °F | UL746B | ||
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL746B | ||
| UL RTI, Mechanical without Impact | 120 °C | 248 °F | UL746B | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||||
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
||||
| 5VA @Thickness 2.30 mm |
5VA @Thickness 0.0906 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |||
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish | |||
| De |
|||||
| Comments | ISO10993 | ||||
| Thin wall V0 & 5VA | |||||
.
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com