| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |||
| Filler Content | 30 % | 30 % | |||
| Water Absorption | 0.20 % | 0.20 % | 24 hrs., 50% RH | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 175 MPa | 25400 psi | |||
| Elongation at Break | 2.6 % | 2.6 % | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | |||
| Flexural Yield Strength | 250 MPa | 36300 psi | |||
| Flexural Modulus | 9.10 GPa | 1320 ksi | |||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | |||
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m² | 27.1 ft-lb/in² | |||
| Charpy Impact Unnotched | 6.80 J/cm² | 32.4 ft-lb/in² | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 6.70e+15 ohm-cm | 6.70e+15 ohm-cm | |||
| Dielectric Constant | 3.2 | 3.2 | |||
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | ASTM D145 | ||
| Dissipation Factor | 0.069 | 0.069 | IEC 60250 | ||
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 | ||
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness 1.50 mm |
7.0 - 15 sec @Thickness 0.0591 in |
UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
|||
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C | 27.2 µin/in-°F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |||
| UL RTI, Electrical | 50.0 °C | 122 °F | UL746B | ||
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL746B | ||
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | 1 - 3 hrs | ||
| De |
|||||
| Comments | High Ductility | ||||
| Nylon/SPS blend | |||||
.