| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |||
| Filler Content | 20 % | 20 % | |||
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | |||
| Elongation at Break | 2.3 % | 2.3 % | |||
| Tensile Modulus | 7.30 GPa | 1060 ksi | |||
| Flexural Yield Strength | 160 MPa | 23200 psi | |||
| Flexural Modulus | 7.00 GPa | 1020 ksi | |||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | |||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |||
| Dielectric Constant | 3.1 | 3.1 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D145 | ||
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 | ||
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 | ||
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 1.50 mm |
15 - 30 sec @Thickness 0.0591 in |
UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
|||
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C | 32.2 µin/in-°F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |||
| UL RTI, Electrical | 110 °C | 230 °F | UL746B | ||
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL746B | ||
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |||
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish | |||
| De |
|||||
| Comments | NSF61 | ||||
.
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com