| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |||
| Filler Content | 30 % | 30 % | |||
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | |||
| Elongation at Break | 2.2 % | 2.2 % | |||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |||
| Flexural Yield Strength | 190 MPa | 27600 psi | |||
| Flexural Modulus | 9.20 GPa | 1330 ksi | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | |||
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | |||
| Charpy Impact Unnotched | 4.60 J/cm² | 21.9 ft-lb/in² | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |||
| Dielectric Constant | 3.1 | 3.1 | |||
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | ASTM D145 | ||
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 | ||
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 | ||
| Hot Wire Ignition, HWI | 30 - 60 sec @Thickness 1.50 mm |
30 - 60 sec @Thickness 0.0591 in |
UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
|||
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C | 31.7 µin/in-°F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |||
| UL RTI, Electrical | 110 °C | 230 °F | UL746B | ||
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL746B | ||
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |||
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish | |||
| De |
|||||
| Comments | NSF61 | ||||
.