顆粒：
物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 | ||
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 | ||
| Flexural Strength | 300 MPa | 43500 psi | ASTM D790 | ||
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D265 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 | ||
| Comparative Tracking Index | 350 V | 350 V | Solution B; IEC 60112 | ||
| 450 V | 450 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 4.50 µm/m-°C @Temperature 23.0 - 85.0 °C |
2.50 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM D696 | ||
| Melting Point | 262 °C | 504 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 0.800 - 3.20 mm |
HB @Thickness 0.0315 - 0.126 in |
|||
| Oxygen Index | 23 % | 23 % | ISO 4589 | ||
| Glow Wire Test | 700 °C @Thickness 1.60 mm |
1290 °F @Thickness 0.0630 in |
IEC-60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |||
| Front Barrel Temperature | 285 - 290 °C | 545 - 554 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 275-285°C | ||||
廣泛用于制造機械、汽車、化學與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包層等。亦可制成薄膜用作包裝材料。此外，還可用于制作醫療器械、體育用品、日用品等。
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。