顆粒圖：
物性表:
用途：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183-A | ||
| Water Absorption | 1.05 % | 1.05 % | 24 hours in water at 23°C; ISO 62. | ||
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | RHODIA-EP | ||
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | RHODIA-EP | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 44.0 MPa | 6380 psi | ISO 527 | ||
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | ISO 527 | ||
| Elongation at Break | 65 % | 65 % | ISO 527 | ||
| Elongation at Yield | 20 % | 20 % | ISO 527 | ||
| Tensile Modulus | 1.90 GPa | 276 ksi | ISO 527 | ||
| Flexural Yield Strength | 70.0 MPa | 10200 psi | ISO 178 | ||
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | Low Temp; ISO 180 | ||
| Izod Impact Resistance | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 180 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/EU-1993 | ||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1EA-1993 | ||
| 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1EA-1993 | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 93 | ||
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
IEC 250 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243-1 | ||
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 | ||
| Comparative Tracking Index | 575 V | 575 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM E831 | ||
| Melting Point | 263 °C | 505 °F | ISO 3146-C | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210/UL 94 | ||
| Oxygen Index | 24.5 % | 24.5 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |||
| Middle Barrel Temperature | 260 - 280 °C | 500 - 536 °F | |||
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Surface | ||
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer | ||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |||
| Fill Speed | 300 - 600 mm/sec | 11.8 - 23.6 in/sec | Peripheral Screw Speed | ||
| De |
|||||
| Injection Speed (cm3/sec) | 80 - 150 cm3/sec | ||||
廣泛應用于機械、儀器儀表、汽車部件、電子電氣、鐵路、家電、通訊、紡機、體育休閑用品、油管、油箱及一些精密工程制品。
電子電器：連接器、卷線軸、計時器、護蓋斷路器、開關殼座。
汽車： 散熱風扇、門把、油箱蓋、進氣隔柵、水箱護蓋、燈座。
工業零件：椅座、自行車輸框、溜冰鞋底座、紡織梭、踏板、滑輸。
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯系人： 夏先生
手 機：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com