- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.07
- 缺口沖擊強度: 0.5
- 拉伸強度 [MPa]: 110.0
- 彎曲模量 [MPa]: 4.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | Amorphous; ISO 1183 | ||
| 1.30 g/cc | 0.0470 lb/in3 | Crystalline; ISO 1183 | |||
| Water Absorption | 0.070 % @Temperature 23.0 °C, Time 86400 sec | 0.070 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 | ||
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 | ||
| Viscosity | 140000 cP @Temperature 400 °C | 140000 cP @Temperature 752 °F | melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | 365°C nozzle, 160°C tool; ISO 294-4 | ||
| Spiral Flow | 220 cm @Thickness 1.00 mm | 86.6 in @Thickness 0.0394 in | 365°C nozzle, 160°C tool | ||
| 250 cm @Thickness 1.00 mm | 98.4 in @Thickness 0.0394 in | 375°C nozzle, 180°C tool | |||
| 300 cm @Thickness 1.00 mm | 118 in @Thickness 0.0394 in | 400°C nozzle, 200°C tool | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 87 @Temperature 23.0 °C | 87 @Temperature 73.4 °F | ISO 868 | ||
| Tensile Strength, Yield | 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 3.90 GPa @Temperature 23.0 °C | 566 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 13.0 MPa @Temperature 275 °C | 1890 psi @Temperature 527 °F | ISO 178 | ||
| 19.0 MPa @Temperature 185 °C | 2760 psi @Temperature 365 °F | ISO 178 | |||
| 21.0 MPa @Temperature 165 °C | 3050 psi @Temperature 329 °F | ISO 178 | |||
| 40.0 MPa @Temperature 150 °C | 5800 psi @Temperature 302 °F | ISO 178 | |||
| 65.0 MPa @Temperature 140 °C | 9430 psi @Temperature 284 °F | ISO 178 | |||
| 90.0 MPa @Temperature 125 °C | 13100 psi @Temperature 257 °F | ISO 178 | |||
| 175 MPa @Temperature 23.0 °C | 25400 psi @Temperature 73.4 °F | ISO 178 | |||
| Flexural Modulus | 4.30 GPa @Temperature 23.0 °C | 624 ksi @Temperature 73.4 °F | ISO 178 | ||
| Compressive Strength | 70.0 MPa @Temperature 120 °C | 10200 psi @Temperature 248 °F | ISO 604 | ||
| 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | ISO 604 | |||
| Izod Impact, Notched (ISO) | 0.500 kJ/m2 @Temperature 23.0 °C | 0.238 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/U | ||
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+9 ohm-cm @Temperature 275 °C | 1.00e+9 ohm-cm @Temperature 527 °F | IEC 60093 | ||
| 1.00e+15 ohm-cm @Temperature 125 °C | 1.00e+15 ohm-cm @Temperature 257 °F | IEC 60093 | |||
| 1.00e+16 ohm-cm @Temperature 23.0 °C | 1.00e+16 ohm-cm @Temperature 73.4 °F | IEC 60093 | |||
| Dielectric Constant | 3.3 @Frequency 50000 Hz, Temperature 23.0 °C | 3.3 @Frequency 50000 Hz, Temperature 73.4 °F | IEC 60250 | ||
| Dielectric Strength | 16.0 kV/mm @Thickness 2.50 mm | 406 kV/in @Thickness 0.0984 in | IEC 60243-1 | ||
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0030 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 | ||
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 μm/m-°C @Temperature <=143 °C | 27.8 μin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 | ||
| 55.0 μm/m-°C @Temperature <=143 °C | 30.6 μin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |||
| 120 μm/m-°C @Temperature >=143 °C | 66.7 μin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |||
| 140 μm/m-°C @Temperature >=143 °C | 77.8 μin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |||
| Specific Heat Capacity | 2.20 J/g-°C @Temperature 23.0 °C | 0.526 BTU/lb-°F @Temperature 73.4 °F | DSC | ||
| Thermal Conductivity | 0.290 W/m-K @Temperature 23.0 °C | 2.01 BTU-in/hr-ft2-°F @Temperature 73.4 °F | ISO/CD 22007-4 | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | ISO 75A-f | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| UL RTI, Electrical | 260 °C | 500 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 180 °C | 356 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |||
| Oxygen Index | 24 % @Thickness 0.400 mm | 24 % @Thickness 0.0157 in | ISO 4239 | ||
| 35 % @Thickness 3.20 mm | 35 % @Thickness 0.126 in | ISO 4239 | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |||
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |||
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||||
| Descriptive Properties | |||||
| Toxicity Index | 0.074 | NES 713; CO content | |||
| 0.15 | NES 713; CO2 content | ||||
| 0.22 | NES 713; Total gases | ||||