- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.04
- 缺口沖擊強(qiáng)度: 5.0
- 彎曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | Crystalline; ISO 1183 |
| Water Absorption | 0.040 % @Temperature 23.0 °C, Time 86400 sec | 0.040 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 |
| Viscosity | 260000 cP @Temperature 400 °C | 260000 cP @Temperature 752 °F | melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | 385°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 16.5 cm @Thickness 1.00 mm | 6.50 in @Thickness 0.0394 in | 385°C nozzle, 180°C tool |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 89 @Temperature 23.0 °C | 89 @Temperature 73.4 °F | ISO 868 |
| Tensile Strength at Break | 180 MPa @Temperature 23.0 °C | 26100 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Break | 1.8 % @Temperature 23.0 °C | 1.8 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 15.0 GPa @Temperature 23.0 °C | 2180 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 270 MPa @Temperature 23.0 °C | 39200 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 14.5 GPa @Temperature 23.0 °C | 2100 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | ISO 180/U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 9.00 μm/m-°C @Temperature <=143 °C | 5.00 μin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 |
| 9.00 μm/m-°C @Temperature >=143 °C | 5.00 μin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |
| 45.0 μm/m-°C @Temperature <=143 °C | 25.0 μin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |
| 110 μm/m-°C @Temperature >=143 °C | 61.1 μin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |
| Specific Heat Capacity | 1.80 J/g-°C @Temperature 23.0 °C | 0.430 BTU/lb-°F @Temperature 73.4 °F | DSC |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||