- 密度 [g/cm3]: 1.3
- 缺口沖擊強(qiáng)度: 4.0
- 拉伸強(qiáng)度 [MPa]: 100.0
- 彎曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 |
| Viscosity | 90000 cP | 90000 cP | melt |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Break | 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 3.70 GPa @Temperature 23.0 °C | 537 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 4.10 GPa @Temperature 23.0 °C | 595 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/U |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |