- 熔體流動速率 [g/10min]: 49.5
- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.06
- 斷裂伸長率 [%]: 210
- 彎曲強(qiáng)度 [MPa]: 140.0
- 彎曲模量 [MPa]: 9.10
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Melt Flow | 49.5 g/10 min @Load 10.0 kg, Temperature 400 °C | 49.5 g/10 min @Load 22.0 lb, Temperature 752 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | |
| Elongation at Break | 2.5 % | 2.5 % | |
| Modulus of Elasticity | 8.30 GPa | 1200 ksi | |
| Flexural Yield Strength | 210 MPa | 30500 psi | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | |
| Compressive Yield Strength | 150 MPa | 21800 psi | |
| Coefficient of Friction, Dynamic | 0.11 | 0.11 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 μm/m-°C @Temperature 100 °C | 12.2 μin/in-°F @Temperature 212 °F | |
| 22.0 μm/m-°C @Temperature 20.0 °C | 12.2 μin/in-°F @Temperature 68.0 °F | ||
| 35.0 μm/m-°C @Temperature 250 °C | 19.4 μin/in-°F @Temperature 482 °F | ||
| Specific Heat Capacity | 1.85 J/g-°C | 0.442 BTU/lb-°F | |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft2-°F | |
| Melting Point | 344 °C | 651 °F | |
| Maximum Service Temperature, Air | 315 °C | 599 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 295 °C | >= 563 °F | |
| Brittleness Temperature | -65.0 °C | -85.0 °F | |
| Glass Transition Temp, Tg | 143 °C | 289 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 43 % | 43 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Middle Barrel Temp |
| Rear Barrel Temperature | 350 °C | 662 °F | |
| Middle Barrel Temperature | 370 °C | 698 °F | |
| Front Barrel Temperature | 380 °C | 716 °F | |
| Nozzle Temperature | 380 °C | 716 °F | |
| Mold Temperature | 180 °C | 356 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3 hour | 3 hour | |
- 關(guān)鍵詞:
- PEEK
- 供應(yīng)
- Victrex? PEEK 150FC30 Easy Flow