- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.12
- 缺口沖擊強度: 0.854
- 拉伸強度 [MPa]: 96.5
- 彎曲模量 [MPa]: 4.10
- 硬度: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | ASTM D792 |
| Water Absorption | 0.12 % @Time 86400 sec | 0.12 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm | 0.016 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm | 1.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 46.8 μm/m-°C | 26.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |