- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.11
- 缺口沖擊強度: 0.98
- 斷裂伸長率 [%]: 250
- 彎曲強度 [MPa]: 156.0
- 彎曲模量 [MPa]: 10.0
- 硬度: 124.0
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in3 | ASTM D792 |
| Water Absorption | 0.11 % | 0.11 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 400 °C | 3.0 g/10 min @Load 11.0 lb, Temperature 752 °F | |
| Spiral Flow | 5.60 cm @Thickness 1.00 mm | 2.20 in @Thickness 0.0394 in | recommended processing conditions |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 103 | 103 | |
| Hardness, Rockwell R | 124 | 124 | |
| Tensile Strength, Ultimate | 156 MPa | 22600 psi | |
| Elongation at Break | 2.7 % | 2.7 % | |
| Modulus of Elasticity | 9.70 GPa | 1410 ksi | |
| Flexural Yield Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | |
| Compressive Yield Strength | 215 MPa | 31200 psi | |
| Poissons Ratio | 0.45 | 0.45 | |
| Shear Modulus | 2.40 GPa | 348 ksi | |
| Shear Strength | 97.0 MPa | 14100 psi | |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | |
| Izod Impact, Unnotched | 3.96 J/cm | 7.42 ft-lb/in | |
| Charpy Impact, Notched | 1.12 J/cm2 | 5.33 ft-lb/in2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | |
| 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | ||
| Dissipation Factor | 0.0010 @Frequency 1000 Hz | 0.0010 @Frequency 1000 Hz | |
| 0.0040 @Frequency 1e+6 Hz | 0.0040 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 μm/m-°C @Temperature 100 °C | 12.2 μin/in-°F @Temperature 212 °F | |
| 22.0 μm/m-°C @Temperature 20.0 °C | 12.2 μin/in-°F @Temperature 68.0 °F | ||
| Specific Heat Capacity | 1.71 J/g-°C | 0.409 BTU/lb-°F | |
| Thermal Conductivity | 0.430 W/m-K | 2.98 BTU-in/hr-ft2-°F | |
| Melting Point | 340 °C | 644 °F | |
| Maximum Service Temperature, Air | 315 °C | 599 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | |
| Brittleness Temperature | -65.0 °C | -85.0 °F | |
| Glass Transition Temp, Tg | 143 °C | 289 °F | |
| UL RTI, Electrical | 240 °C | 464 °F | |
| UL RTI, Mechanical with Impact | 220 °C | 428 °F | |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 380 °C | 716 °F | Middle Barrel Temp |
| Rear Barrel Temperature | 360 °C | 680 °F | |
| Middle Barrel Temperature | 380 °C | 716 °F | |
| Front Barrel Temperature | 390 °C | 734 °F | |
| Nozzle Temperature | 390 °C | 734 °F | |
| Mold Temperature | 180 °C | 356 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3 hour | 3 hour | |