- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 1.07
- 拉伸強度 [MPa]: 207.0
- 彎曲模量 [MPa]: 18.6
- 硬度: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec | 0.15 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.17 mm | 0.0010 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 310 MPa | 45000 psi | ASTM D790 |
| Flexural Modulus | 18.6 GPa | 2700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm | 2.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 10.8 μm/m-°C | 6.00 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 288 °C | 550 °F | Unannealed; ASTM D648 |