- 密度 [g/cm3]: 1.37
- 缺口沖擊強度: 0.84
- 拉伸強度 [MPa]: 76.0
- 彎曲模量 [MPa]: 3.07
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec | 0.0030 - 0.0050 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
| 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 |
| 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 17.8 % | 17.8 % | 5 mm/min; ISO 527 |
| 52 % | 52 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.28 GPa | 476 ksi | 1 mm/min; ISO 527 |
| 3.33 GPa | 483 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 3.07 GPa | 445 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.12 GPa | 453 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 29.9 J/cm | 56.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 158 kJ/m2 | 75.2 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C | 3.69 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 42.3 x 10-8 mm3/N-M | 21.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 166 °C @Thickness 3.20 mm | 331 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 3.20 mm | 300 °F @Thickness 0.126 in | unannealed; ASTM D648 | |