- 密度 [g/cm3]: 1.64
- 缺口沖擊強度: 1.03
- 拉伸強度 [MPa]: 176.0
- 彎曲模量 [MPa]: 11.36
- 熱變形溫度 [℃]: 337.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 170 MPa | 24700 psi | Type I, 5 mm/min; ASTM D638 |
| 177 MPa | 25700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 176 MPa | 25500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 12.24 GPa | 1775 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 263 MPa | 38100 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.36 GPa | 1648 ksi | 2 mm/min; ISO 178 |
| 11.7 GPa | 1700 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.03 J/cm | 1.93 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.61 J/cm | 16.1 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C | 9.59 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.49 | 0.49 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.73 | 0.73 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm3/N-M | 9.00 x 10-10 in3-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 129 x 10-8 mm3/N-M | 64.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 10.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 36.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 20.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 337 °C | 639 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 339 °C @Thickness 3.20 mm | 642 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 322 °C | 612 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 327 °C @Thickness 3.20 mm | 621 °F @Thickness 0.126 in | unannealed; ASTM D648 | |