- 缺口沖擊強度: 0.69
- 彎曲模量 [MPa]: 13.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Melt Index of Compound | 30 g/10 min @Load 5.00 kg, Temperature 300 °C | 30 g/10 min @Load 11.0 lb, Temperature 572 °F | MVR [cm^3/10 min]; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 181 MPa | 26300 psi | 5 mm/min; ISO 527 |
| 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.96 GPa | 2025 ksi | 1 mm/min; ISO 527 |
| 16.0 GPa | 2320 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 276 MPa | 40000 psi | ISO 178 |
| 277 MPa | 40200 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 13.4 GPa | 1940 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.53 GPa | 1962 ksi | 2 mm/min; ISO 178 | |
| Poissons Ratio | 0.43 | 0.43 | ISO 527-1/2 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.37 | 0.37 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm3/N-M | 14.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 32.0 °C @Thickness 3.20 mm | 89.6 °F @Thickness 0.126 in | unannealed; ASTM D648 |