- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.1
- 拉伸強度 [MPa]: 165.0
- 彎曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Thickness 3.18 mm | 0.10 % @Thickness 0.125 in | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 165 MPa | 23900 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 11.7 GPa | 1700 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 310 °C @Thickness 3.18 mm | 590 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 388 - 399 °C | 730 - 750 °F | |||
| Descriptive Properties | |||||
| Features | General Purpose | ||||
| High Heat Resistance | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | PEEK | ||||
| Generic Name | Polyetheretherketone (PEEK) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Automotive Applications | ||||
| Consumer Applications | |||||
| General Purpose | |||||
| Industrial Applications | |||||