- 吸水率 [%]: 0.07
- 缺口沖擊強度: 0.908
- 拉伸強度 [MPa]: 241.0
- 彎曲模量 [MPa]: 20.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Thickness 3.17 mm | 0.070 % @Thickness 0.125 in | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.00050 - 0.0010 cm/cm | 0.00050 - 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 241 MPa | 35000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 20.7 GPa | 3000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 310 MPa | 45000 psi | ASTM D790 |
| Flexural Modulus | 20.7 GPa | 3000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 1.70 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 316 °C | 600 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 388 - 399 °C | 730 - 750 °F | Molding |