- 拉伸強度 [MPa]: 89.6
- 彎曲模量 [MPa]: 3.69
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 | ||
| Deformation | 0.14 % | 0.14 % | ASTM D621 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 96 | 96 | ASTM D785 | ||
| Hardness, Shore D | 85 | 85 | ASTM D2240 | ||
| Tensile Strength at Break | 86.9 MPa | 12600 psi | ASTM D368 | ||
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 | ||
| Elongation at Break | 20 % | 20 % | ASTM D638 | ||
| Flexural Strength | 145 MPa | 21100 psi | ASTM D790 | ||
| Flexural Modulus | 3.69 GPa | 535 ksi | Flexural 0.5% Secant Modulus; ASTM D790 | ||
| 0.2031 GPa @Temperature 204 °C | 29.46 ksi @Temperature 400 °F | ||||
| Compressive Strength | 107 MPa | 15500 psi | ASTM D695 | ||
| Shear Strength | 71.7 MPa | 10400 psi | Axial; ASTM D732 | ||
| 71.7 MPa | 10400 psi | Transverse; ASTM D732 | |||
| 14.3 MPa @Temperature 288 °C | 2080 psi @Temperature 550 °F | ||||
| 48.7 MPa @Temperature 149 °C | 7070 psi @Temperature 300 °F | ||||
| 68.3 MPa @Temperature 65.6 °C | 9900 psi @Temperature 150 °F | ||||
| Secant Modulus | 3.59 GPa | 521 ksi | Tensile 0.5% Secant Modulus; ASTM D638 | ||
| Coefficient of Friction, Dynamic | 0.15 | 0.15 | PV=12600 psi-ft./min.; ASTM G77 | ||
| K (wear) Factor | 40.3 x 10-8 mm3/N-M | 20.0 x 10-10 in3-min/ft-lb-hr | ASTM G77 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 41.4 μm/m-°C @Temperature <=149 °C | 23.0 μin/in-°F @Temperature <=300 °F | ASTM E228 | ||
| 148 μm/m-°C @Temperature >=149 °C | 82.0 μin/in-°F @Temperature >=300 °F | ASTM E228 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 330 °F | |||
| Descriptive Properties | |||||
| Color | Tan | ||||