- 吸水率 [%]: 0.2
- 缺口沖擊強(qiáng)度: 0.75
- 拉伸強(qiáng)度 [MPa]: 124.0
- 彎曲模量 [MPa]: 5.17
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % @Thickness 3.18 mm | 0.20 % @Thickness 0.125 in | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 124 MPa | 18000 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 5.52 GPa | 801 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 | ||
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 1.41 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 3.18 mm | 410 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 377 - 388 °C | 711 - 730 °F | |||
| Descriptive Properties | |||||
| Features | General Purpose | ||||
| High Heat Resistance | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 10% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | PEEK | ||||
| Generic Name | Polyetheretherketone (PEEK) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Automotive Applications | ||||
| Consumer Applications | |||||
| General Purpose | |||||
| Industrial Applications | |||||