- 吸水率 [%]: 0.2
- 缺口沖擊強度: 1.23
- 拉伸強度 [MPa]: 150.0
- 彎曲模量 [MPa]: 7.86
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | ASTM D638 |
| Elongation at Yield | 3.6 % | 3.6 % | ASTM D638 |
| Tensile Modulus | 8.41 GPa | 1220 ksi | ASTM D638 |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.18 mm | 2.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 11.2 J/cm @Thickness 3.18 mm | 21.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.70 kJ/m2 | 4.62 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 71.8 kJ/m2 | 34.2 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 9.93 J | 7.32 ft-lb | ASTM D3763 |
| Impact Test | 2.72 J | 2.01 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 31.0 μm/m-°C @Temperature 20.0 °C | 17.2 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 72.0 μm/m-°C @Temperature 20.0 °C | 40.0 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |