- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.17
- 拉伸強度 [MPa]: 149.0
- 彎曲模量 [MPa]: 8.48
- 熱變形溫度 [℃]: 224.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | Method A; ASTM D792 | ||
| Density | 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 149 MPa | 21600 psi | ASTM D638 | ||
| Tensile Strength, Yield | 149 MPa | 21600 psi | ASTM D638 | ||
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 | ||
| Elongation at Yield | 2.6 % | 2.6 % | ASTM D638 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 | ||
| Flexural Strength | 221 MPa | 32100 psi | ASTM D790 | ||
| Flexural Modulus | 8.48 GPa | 1230 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.18 mm | 2.19 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Izod Impact, Unnotched | 9.39 J/cm @Thickness 3.18 mm | 17.6 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m2 | 30.9 ft-lb/in2 | ISO 180 | ||
| Falling Dart Impact | 8.50 J | 6.27 ft-lb | ASTM D3763 | ||
| Impact Test | 3.19 J | 2.35 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 | ||
| Coefficient of Friction, Dynamic | 0.71 | 0.71 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.52 | 0.52 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 | ||
| K (wear) Factor | 30.2 x 10-8 mm3/N-M | 15.0 x 10-10 in3-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |||
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.20 % | 0.20 % | Suggested | ||
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |||
| Descriptive Properties | |||||
| Color | Black | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.