- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.16
- 缺口沖擊強度: 1.12
- 斷裂伸長率 [%]: 195
- 彎曲模量 [MPa]: 7.58
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Water Absorption | 0.16 % @Time 86400 sec | 0.16 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm | 0.0050 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 117 MPa | 17000 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 195 MPa | 28300 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm @Thickness 3.17 mm | 2.10 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm @Thickness 3.17 mm | 16.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.0 μm/m-°C | 15.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |