- 吸水率 [%]: 0.17
- 缺口沖擊強(qiáng)度: 1.87
- 彎曲模量 [MPa]: 9.65
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 | ||
| Water Absorption | 0.17 % | 0.17 % | 24 hr; ASTM D750 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 183 MPa | 26500 psi | ASTM D638 | ||
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 | ||
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 | ||
| Flexural Strength | 259 MPa | 37500 psi | ASTM D790 | ||
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.87 J/cm @Temperature 22.8 °C | 3.50 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | |||
| Oxygen Index | 25 % | 25 % | ASTM D2863 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 235 - 252 °C | 455 - 485 °F | |||
| Middle Barrel Temperature | 246 - 268 °C | 475 - 515 °F | |||
| Front Barrel Temperature | 257 - 274 °C | 495 - 525 °F | |||
| Nozzle Temperature | 252 - 279 °C | 485 - 535 °F | |||
| Melt Temperature | 223 °C | 433 °F | |||
| 252 - 277 °C | 485 - 530 °F | Processing Temperature | |||
| Drying Temperature | 79.4 °C | 175 °F | |||
| Descriptive Properties | |||||
| Suggested Moisture, max | 0.2 | ||||
| Suggested Regrind, max | 25 | ||||