- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.76
- 拉伸強度 [MPa]: 192.0
- 彎曲模量 [MPa]: 9.03
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | Method A; ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 |
| Water Absorption | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
| Tensile Strength, Yield | 192 MPa | 27800 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Elongation at Yield | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 11.9 GPa | 1730 ksi | ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 9.03 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm @Thickness 3.18 mm | 3.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 13.7 J/cm @Thickness 3.18 mm | 25.7 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 16.9 kJ/m2 | 8.04 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 88.3 kJ/m2 | 42.0 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 11.8 J | 8.70 ft-lb | ASTM D3763 |
| Impact Test | 4.76 J | 3.51 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |