- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.25
- 缺口沖擊強度: 15.0
- 斷裂伸長率 [%]: 290
- 彎曲模量 [MPa]: 15.2
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ISO 1183 |
| Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 196 MPa | 28400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 18.7 GPa | 2710 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 280 MPa | 40600 psi | break, 2 mm/min; ISO 178 |
| Flexural Yield Strength | 290 MPa | 42100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.2 GPa | 2200 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m2 | 30.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 7.40 μm/m-°C @Temperature 23.0 - 60.0 °C | 4.11 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 95.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 52.8 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |