- 密度 [g/cm3]: 1.56
- 缺口沖擊強度: 0.64
- 拉伸強度 [MPa]: 145.0
- 彎曲模量 [MPa]: 9.00
- 熱變形溫度 [℃]: 218.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ASTM D792 |
| 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm @Time 86400 sec | 0.0029 in/in @Time 24.0 hour | ISO 294 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0086 cm/cm @Time 86400 sec | 0.0086 in/in @Time 24.0 hour | ISO 294 |
| 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 |
| 150 MPa | 21800 psi | ASTM D638 | |
| Tensile Strength, Yield | 145 MPa | 21000 psi | ISO 527 |
| 150 MPa | 21800 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Elongation at Yield | 1.8 % | 1.8 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 11.02 GPa | 1598 ksi | 1 mm/min; ISO 527 |
| 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 197 MPa | 28600 psi | ISO 178 |
| 199 MPa | 28900 psi | ASTM D790 | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| 9.65 GPa | 1400 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.03 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m2 | 17.6 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 66.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 37.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 67.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 37.2 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 39.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 22.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 40.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 22.2 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm | 428 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm | 394 °F @Thickness 0.126 in | unannealed; ASTM D648 | |