- 密度 [g/cm3]: 1.25
- 彎曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 Type 1A | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 Type 1A | ||
| Tensile Modulus | 7.40 GPa | 1070 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 199 MPa | 28900 psi | ISO 178 | ||
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| 10.0 J/cm2 @Temperature -30.0 °C | 47.6 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.70 J/cm2 @Temperature 23.0 °C | 12.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ISO 1210 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ISO 1210 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ISO 1210 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |||
| Melt Temperature | 215 °C | 419 °F | ISO 11357 | ||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 230-240°C | ||||
| Mixing Zone | 240-250°C | ||||