- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.1
- 彎曲模量 [MPa]: 1.67
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | STN EN ISO 1183-1 | ||
| Melt Flow | 4.0 g/10 min @Load 0.325 kg, Temperature 275 °C | 4.0 g/10 min @Load 0.716 lb, Temperature 527 °F | STN EN ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | STN EN ISO 527-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | STN EN ISO 527-2 | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | STN EN ISO 527-2 | ||
| Flexural Strength | 72.0 MPa | 10400 psi | STN EN ISO 178 | ||
| Flexural Modulus | 1.67 GPa | 242 ksi | STN EN ISO 178 | ||
| Charpy Impact Unnotched | 3.00 J/cm2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | STN EN ISO 179 | ||
| 4.50 J/cm2 @Temperature -20.0 °C | 21.4 ft-lb/in2 @Temperature -4.00 °F | STN EN ISO 179 | |||
| Charpy Impact, Notched | 0.360 J/cm2 @Temperature -20.0 °C | 1.71 ft-lb/in2 @Temperature -4.00 °F | STN EN ISO 179 | ||
| 0.370 J/cm2 @Temperature 23.0 °C | 1.76 ft-lb/in2 @Temperature 73.4 °F | STN EN ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 215 °C | 419 °F | STN EN 11357-1 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Drying Temperature | 80.0 °C @Time 14400 sec | 176 °F @Time 4.00 hour | |||
| Moisture Content | 0.25 % | 0.25 % | STN EN ISO 3344 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||