- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.4
- 缺口沖擊強(qiáng)度: 0.8
- 彎曲強(qiáng)度 [MPa]: 66.0
- 彎曲模量 [MPa]: 1.90
- 硬度: 112.0
- 熱變形溫度 [℃]: 174.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 °C | 421 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ASTM D648 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA610
- Ashley Polymers Ashlene? 990L Nylon 610