- 密度 [g/cm3]: 1.52
- 缺口沖擊強度: 1.87
- 拉伸強度 [MPa]: 193.0
- 彎曲模量 [MPa]: 10.4
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm | 3.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |