- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 1.87
- 斷裂伸長率 [%]: 207
- 彎曲強(qiáng)度 [MPa]: 131.0
- 彎曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 6.90 GPa | 1000 ksi | ASTM D638 |
| Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Thickness 6.35 mm | 3.50 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 48.6 μm/m-°C @Temperature 20.0 °C | 27.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | Stock |
| Mold Temperature | 93.0 °C | 199 °F | |
| Drying Temperature | 77.0 °C | 171 °F | |