- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 1.71
- 斷裂伸長率 [%]: 221
- 彎曲強度 [MPa]: 145.0
- 彎曲模量 [MPa]: 7.60
- 硬度: 119.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Flexural Yield Strength | 221 MPa | 32100 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Yield Strength | 123 MPa | 17800 psi | ASTM D695 |
| Shear Strength | 72.0 MPa | 10400 psi | ASTM D732 |
| Izod Impact, Notched | 1.71 J/cm @Thickness 6.35 mm | 3.20 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 28.8 μm/m-°C @Temperature 20.0 °C | 16.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 288 °C | 520 - 550 °F | Stock |
| Mold Temperature | 93.0 - 107 °C | 199 - 225 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |